Damage Condition Possible Causes Countermeasures
Dull or cloudy spots appear on surface along with light wear. From such dull spots, tiny cracks are generated downward to a depth of 5-10 μm. Small particles fall off and minor flaking occurs widely.
  • Unsuitable lubricant
  • Entry of debris into lubrication
  • Rough surface due to poor lubrication
  • Surface roughness of mating rolling parts
  • Select a proper lubricant
  • Improve the sealing mechanism
  • Improve the surface finish of the rolling mating parts

 

Click a photo to enlarge it

Peeling 1

Part: Inner ring of a spherical roller bearing
Symptom: Rounded areas of Peeling
Cause: Poor lubrication

Peeling 2

Part: Enlargement of damage “Peeling 1”

Peeling 3

Part: Convex rollers of damage “Peeling 1”
Symptom: Rounded areas of Peeling on the center of the rolling surfaces
Cause: Poor lubrication

Peeling 4

Part: Outer ring of a spherical roller bearing
Light Experience Arctic C Multicoloured Running Shoes Women’s Punch NIKE Gs Rn Flex 600 7
Symptom: Peeling occurs near the shoulder of the raceway over the entire circumference
Cause: Poor lubrication

Downloads

Order Files

Shoes 600 Punch 7 Running Flex Light C Women’s Gs Rn Multicoloured NIKE Experience Arctic wxOq10U1 Shoes 600 Punch 7 Running Flex Light C Women’s Gs Rn Multicoloured NIKE Experience Arctic wxOq10U1 Shoes 600 Punch 7 Running Flex Light C Women’s Gs Rn Multicoloured NIKE Experience Arctic wxOq10U1 Shoes 600 Punch 7 Running Flex Light C Women’s Gs Rn Multicoloured NIKE Experience Arctic wxOq10U1 Shoes 600 Punch 7 Running Flex Light C Women’s Gs Rn Multicoloured NIKE Experience Arctic wxOq10U1

Cookies on the NSK website

We use cookies to ensure that we give you the best experience on our websites and web applications. By continuing without changing your browser settings, we assume you give your consent to receive cookies. However, you can change your browser cookie setting at any time.